Fracture Resistance of the Bundle Post System and Conventional Fiber Post with Different Lengths.

This study compares the fracture strength of teeth restored with conventional round fiber post (CP) and bundle post (BP) in two different lengths. A total of 48 mandibular premolars were selected. Endodontic treatment was performed, and the premolars were divided into four groups (n = 12 per group): Group C9 = 9-mm CP; Group C5 = 5-mm CP; Group B9 = 9-mm BP; Group B5 = 5-mm BP. Post spaces were prepared, and posts were disinfected with alcohol. Silane was applied, and posts were placed with self-etch dual-cure adhesive. The core structures were created using dual-cure adhesive and standardized core-matrix. Specimens were embedded in acrylic, and the periodontal ligament was simulated with polyvinyl-siloxane impression material. Thermocycling was performed, and specimens were then loaded at a 45-degree angle to the long axis. The failure mode was analyzed with ×5 magnification, and statistical analyses were performed. No statistical difference was found between post systems and post lengths (P > .05). Chi-square test revealed no statistical difference in the failure mode (P > .05). BP did not affect fracture resistance compared to CP. For the restoration of extremely irregular canals with a fiber post, BP can be used as an alternative system because it does not reduce the fracture strength. If necessary, longer posts can be used without decreasing the fracture resistance.

In vivo vs. in vitro color stability of hybrid ceramic and resin nanoceramic blocks used for endocrowns: A new method.

PURPOSE: To evaluate and compare in vitro and in vivo color parameters of hybrid ceramic, resin nanoceramic, and artificial acrylic resin teeth. METHODS: For the in vitro stages, 120 specimens (2 mm) were prepared from Vita Enamic (VE), Lava Ultimate (LU), CeraSmart (CS), and acrylic teeth (IV), and immersed in coffee, red wine, and distilled water for 24, 72, and 144 hours. For the in vivo stage, 16 individuals received a complete denture that had upper premolars made of VE, LU, CS blocks, and IV. The color was measured at 1, 3, and 6 months. Color difference (ΔE00), translucency (TP), and contrast ratio (CR) were obtained using a spectrophotometer. Shapiro Wilk, one-way ANOVA, and repeated measures ANOVA were used for statistical analysis. RESULTS: ΔE00 of VE and LU were higher than CS and IV (P< 0.05). ΔTP of VE and LU were lower than CS and IV (P< 0.05). ΔTP of CS was higher in red wine compared to coffee. ΔCR of CS and IV were increased with prolonged immersion (P< 0.001). ΔE00 and ΔCR were similarly affected in coffee and red wine. All discolorations were higher than clinical acceptability (ΔE00> 1.77). For in vivo stages, ΔE00 of VE and LU increased over time (P< 0.01). No difference was detected between in vivo and in vitro ΔE00 of CS (P> 0.05). ΔE00 of VE, LU, and IV was higher in in vitro stages. LU and VE showed lower color stability; their use in esthetic regions is questionable. The prolonged immersion increased discoloration. Coffee and red wine had a similar effect on discoloration and opalescence. Discoloration in laboratory conditions did not correspond to the clinical discoloration according to the new method presented in this study. CLINICAL SIGNIFICANCE: The use of CAD-CAM blocks for endocrowns is rising; however, Lava Ultimate and Vita Enamic showed lower color stability, thus, their use in esthetic regions is questionable. This is the first study that investigates the discoloration of CAD-CAM blocks in clinical use. Discoloration in laboratory conditions did not correspond to the clinical discoloration.

Effect of Different Surface Treatments Applied to Short Zirconia and Titanium Abutments.

PURPOSE: The aim of this study was to compare the effect of different surface treatments applied to short titanium and zirconia abutments on the bond strength of single-unit zirconia crowns. MATERIALS AND METHODS: Sixty titanium abutments were shortened to 3 mm in length, fixed to analogs, and embedded in acrylic blocks. Three-dimensional views of abutments were obtained by scanning; then, zirconia abutments and copings were produced. The samples, which included titanium (n = 60) and zirconia (n = 60) abutments, were divided into five different groups (n = 12), and surface treatments were carried out; 1.5-W and 3-W Er,Cr:YSGG laser treatment, AL2O3 sandblasting, and tribochemical silica coating were applied to the groups, and the control group had no surface treatment. Copings were cemented to the samples with self-adhesive resin cement. The samples were then subjected to the pull-out test, and the results were processed via statistical analysis. RESULTS: There was a significant difference between the titanium and zirconia groups (P < .001). The mean bond strength values of the titanium samples were higher than those of the zirconia samples. The tribochemical silica coating gave a higher bond strength than the other treatments when applied to titanium abutments. For the zirconia abutments, the 1.5-W laser treatment, 3-W laser treatment, tribochemical silica coating, and Al2O3 sandblasting groups differed significantly from the control group; however, they were not significantly different from each other. CONCLUSION: The bond strength of zirconia crowns to short titanium and zirconia abutments increases with surface treatments. Furthermore, the surface treatments were more effective in increasing the bond strength for the titanium abutments than for the zirconia abutments.

Evaluation of the Bond Strengths between Dental Porcelain and Cobalt-Chromium Metal Frameworks Manufactured with Different Techniques after the Thermal Aging Process.

PURPOSE: The present study is aimed at examining the bond strength of cobalt-chromium (Co-Cr) metal frameworks, prepared through different techniques, to a single type of low-temperature porcelain system after the thermal aging process. METHODS: A hundred and twenty Co-Cr alloy framework specimens were prepared using conventional casting, CAD/CAM, and two commercially different laser sintering devices, and dental porcelain was applied to the specimens. A single type of dental porcelain (Kuraray Noritake Dental Inc., Tokyo, Japan) was applied to the specimens. After the subgroups were determined, half of the specimens were subjected to a thermal aging process. Bond strength of specimens was evaluated using a 3-point bending test. The surfaces of the fractured specimens were evaluated using a stereomicroscope. The metal-porcelain bonding area of samples randomly selected from 8 groups has been examined with SEM under ×1000 magnifications. Normality distribution of obtained data was examined using by a Kolmogorov-Smirnov test. The obtained data of the present study was statistically analyzed with a statistical package program (SPSS for Windows 22.0, Chicago, IL, USA). RESULTS: There was a statistically significant difference between CAD/CAM and the other three methods, and the bonding value of the CAD/CAM group was the highest among the groups. Besides, the bond strength between dental porcelain and 4 differently produced metal frameworks was high enough to surpass the acceptable threshold (>25 MPa) according to the ISO 9693. There was no statistically significant difference between thermal aging applied and nonapplied groups. CONCLUSIONS: Based on this study, it could be shown that the metal-ceramic bond strength is dependent on the manufacturing method used, but it is independent of the thermal aging application. It was found that the bond strength values of all samples with and without thermal aging application exceeded the minimum acceptable value of 25 MPa recommended by the ISO 9693.

Finite Element Stress Analysis of Applied Forces to Implants and Supporting Tissues Using the "All-on-Four" Concept with Different Occlusal Schemes.

PURPOSE: The aim of this study was to evaluate stress distributions on implants and alveolar bone due to occlusal load produced during chewing by prostheses prepared according to the All-on-Four concept with different occlusal schemes using a finite element analysis method. MATERIALS AND METHODS: On standard jaw models, teeth were set in accordance with the basic standards of canine-guided occlusion, group function occlusion, bilateral balanced occlusion (BBO), lingualized occlusion, and monoplane occlusion schemes. Three-dimensional (3D) images of these models were obtained using a surface scanner. Implants, superstructures, the maxilla, and mandible were modeled in the All-on-Four concept with 3D modeling software. Forces were defined on contacts formed in maximum intercuspation, lateral, and protrusive movement position for all 5 occlusion types. Stress outputs were recorded as maximum and minimum principal stresses (Pmax , Pmin ) and von Mises stress values for the implants. RESULTS: The highest Pmax value for the maxilla was observed in cortical bone in the group function occlusion during lateral movement (15.56 MPa). For the mandible, the highest Pmax value was observed on the cortical bone in maximum intercuspation of lingualized occlusion (72.75 MPa). The highest Pmin value for the maxilla was observed during the lateral movement in group function and for the mandible in BBO (-29.23 and -86.31 MPa, respectively). The lowest stress values were observed with canine-guided occlusion in all related conditions and on all structures. CONCLUSIONS: With the limitations of this simulation study, considering stresses on alveolar bone and implants in All-on-Four applications, the use of canine-guided occlusion may be suggested.